It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa ⋅ m 3 / kg , or N ⋅m/kg, which is dimensionally equivalent to m 2 /s 2 , though the latter form is rarely used.
Specific modulus: Modulus per unit volume (MPa/m^3) Specific strength: Strength per unit density (Nm/kg) Specific weight: Weight per unit volume (N/m^3) Surface roughness: The deviations in the direction of the normal vector of a real surface from its ideal form; Tensile strength: Maximum tensile stress of a material can withstand before ...
Specific modulus is a materials property consisting of the elastic modulus per mass density of a material. It is also known as the stiffness to weight ratio or specific stiffness . High specific modulus materials find wide application in aerospace applications where minimum structural weight is required.
Elastic properties describe the reversible deformation (elastic response) of a material to an applied stress.They are a subset of the material properties that provide a quantitative description of the characteristics of a material, like its strength.
Since carbon nanotubes have a low density for a solid of 1.3 to 1.4 g/cm 3, its specific strength of up to 48,000 kN·m·kg −1 is the best of known materials, compared to high-carbon steel's 154 kN·m·kg −1. Under excessive tensile strain, the tubes will undergo plastic deformation, which means the deformation is permanent. This ...
The ultimate strength is the maximum stress that a material can withstand before it breaks or weakens. [12] For example, the ultimate tensile strength (UTS) of AISI 1018 Steel is 440 MPa. In Imperial units, the unit of stress is given as lbf/in 2 or pounds-force per square inch. This unit is often abbreviated as psi.
By comparison, annealed type 316 stainless steel has a density of 8000 kg/m 3, modulus of 193 GPa, and tensile strength of 570 MPa. [23] Tempered 6061 aluminium alloy has a density of 2700 kg/m 3, modulus of 69 GPa, and tensile strength of 310 MPa, respectively. [24] Ti-6Al-4V standard specifications include: [25] [26]
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [9] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.