Whether stainless steel corrodes depends on the kind and concentration of acid or base and the solution temperature. Uniform corrosion is typically easy to avoid because of extensive published corrosion data or easily performed laboratory corrosion testing. Stainless steel is not completely immune to corrosion, as shown in this desalination ...
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. PREN is frequently specified when stainless steels will be exposed to seawater or other high chloride solutions. In some instances stainless steels with PREN-values > 32 may provide useful resistance to pitting corrosion in ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
This metal is commonly used instead of 300 series stainless steels in high temperature and low pH applications in food processing. For example, tomato juice will corrode 316L stainless steel at pasteurization temperatures of 100 °C (210 °F). AL-6XN will better resist this corrosion while still offering the beneficial properties of stainless ...