Hot-dip galvanizing deposits a thick, robust layer of zinc iron alloys on the surface of a steel item. In the case of automobile bodies, where additional decorative coatings of paint will be applied, a thinner form of galvanizing is applied by electrogalvanizing .
Zinc coated steel substrate for PPGI is typically produced on a continuous galvanizing line (CGL). The CGL may include a painting section after the hot dip galvanising section, or more commonly the metallic coated substrate in coil form is processed on a separate continuous paint line (CPL).
Because electrolytically zinc-plated surfaces provide comparatively little corrosion protection, and in the case of galvanic zinc coatings on high-strength steel (e.g. category 10.9 and 12.9 high-strength bolts) there is a risk of hydrogen embrittlement, the industry needed a better corrosion protection system.
Galvanized steel can be welded; however, one must exercise caution around the resulting toxic zinc fumes. Galvanized fumes are released when the galvanized metal reaches a certain temperature. This temperature varies by the galvanization process used. In long-term, continuous exposure, the recommended maximum temperature for hot-dip galvanized ...
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
Using the same metal for all construction is the easiest way of matching potentials. Electroplating or other plating can also help. This tends to use more noble metals that resist corrosion better. Chrome, nickel, silver and gold can all be used. Galvanizing with zinc protects the steel base metal by sacrificial anodic action.
The most common conversion coating processes for metal parts with industrial use include Chromate (aluminum, steel) Phosphate (steel) Bluing (steel) Black oxide (steel) Anodizing (aluminum) Stannate (magnesium) [5] Molybdate (zinc, zinc-nickel) [6] [7] Zirconate (steel, aluminum, magnesium, galvanized steel). [1] [8] [9] Titanate (steel ...