T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
2014 aluminium alloy is a strong and hard aluminium-based alloy used in the aerospace industry. It has poor corrosion resistance and is difficult to weld, and is often clad or painted.
Hiduminium is a series of high-strength, high-temperature aluminium alloys developed by Rolls-Royce before World War II. RR56 is one of the alloys used for pistons, crankcases and compressors in aero engines and jet engines.
6060 aluminium alloy is a wrought aluminium-magnesium-silicon alloy with various tempers and applications. It has the alternate names AlMgSi, 3.3206, and A96060, and is covered by several standards.
2017 aluminium alloy is a copper-containing aluminium alloy with good corrosion resistance and mechanical properties. It has a chemical composition of 91.5-95.5% aluminium, 3.5-4.5% copper, and other elements.
6061 is a precipitation-hardened aluminium alloy with magnesium and silicon as major alloying elements. It has good mechanical properties, weldability and extrudability, and is widely used for aircraft structures, automotive parts and other applications.
6082 aluminium alloy is a wrought aluminium-magnesium-silicon alloy with various tempers and applications. It has a chemical composition of 95.2 to 98.3% aluminium, 0.6 to 1.2% magnesium, and 0.4 to 1.0% manganese.
7075 aluminium alloy is a zinc-based alloy with excellent mechanical properties and corrosion resistance. It is widely used in aircraft structural parts and has various tempers, such as T6, T651, and T7.