Reactive powder concrete, also known as ultra-high-performance concrete, can be even stronger, with strengths of up to 800 MPa (116,000 PSI). [4] These are made by eliminating large aggregate completely, carefully controlling the size of the fine aggregates to ensure the best possible packing, and incorporating steel fibers (sometimes produced ...
Pervious concrete has a common strength of 600–1,500 pounds per square inch (4.1–10.3 MPa) though strengths up to 4,000 psi (28 MPa) can be reached. There is no standardized test for compressive strength. [15] Acceptance is based on the unit weight of a sample of poured concrete using ASTM standard no. C1688. [16]
Regular concrete can typically withstand a pressure from about 10 MPa (1450 psi) to 40 MPa (5800 psi), with lighter duty uses such as blinding concrete having a much lower MPa rating than structural concrete. Many types of pre-mixed concrete are available which include powdered cement mixed with an aggregate, needing only water.
When creating hydrophobic concrete through a coating process, a coating is sprayed or brushed onto a porous surfaces. In most cases, it is applied to a regular concrete slab that then undergoes a corrosive process to expose more of the concrete's capillaries. This can be achieved by water blasting the surface at about 3,000-4,000 psi.
Lightweight concrete is often achieved by adding air, foams, or lightweight aggregates, with the side effect that the strength is reduced. For most routine uses, 20 to 32 MPa (2,900 to 4,600 psi) concrete is often used. 40 MPa (5,800 psi) concrete is readily commercially available as a more durable, although more expensive, option.
1920 – Effect of Tannic Acid on Strength of Concrete ; 1921 – Quantities of Materials for Concrete, D. A. Abrams en Stanton Walker (Recipes for concrete reporting its strength after 28 days of curing ranging from 2000 to 4000 psi). 1922 – Flexural Strength of Plain Concrete (Relationship between flexural strength and compressive strength)
A benefit of pre-topped double tees is a higher quality concrete for more durable surface to reduce traffic wears. Factories can produce the topping with minimum concrete strength of 5,000 psi. In some areas, the strength can be 6,000-8,000 psi. This compares to the field-placed concrete topping with the lower concrete strength of 4,000 psi. [6]
The mix design of the concrete should be 3500 psi or higher. The concrete should be poured full depth to take advantage of the concrete's full structural strength, and also help to prevent cracks. The concrete should always be professionally finished with power trowels and cured with water for seven days. Polishing should not begin until the ...