Isothermal transformation diagrams (also known as time-temperature-transformation (TTT) diagrams) are plots of temperature versus time (usually on a logarithmic scale). They are generated from percentage transformation-vs time measurements, and are useful for understanding the transformations of an alloy steel at elevated temperatures.
Tempering at a slightly elevated temperature for a shorter time may produce the same effect as tempering at a lower temperature for a longer time. Tempering times vary, depending on the carbon content, size, and desired application of the steel, but typically range from a few minutes to a few hours. Tempering quenched steel at very low ...
Normalizing not only produces pearlite but also martensite and sometimes bainite, which gives harder and stronger steel but with less ductility for the same composition than full annealing. In the normalizing process the steel is heated to about 40 degrees Celsius above its upper critical temperature limit, held at this temperature for some ...
Eventually, a maximum yield strength is reached. For even higher temperatures, the yield strength decreases and, eventually, drops to zero when reaching the melting temperature, where the solid material transforms into a liquid. For ordered intermetallics, the temperature of the yield strength peak is roughly 50% of the absolute melting ...
No tempering is required after austempering if the part is through hardened and fully transformed to either Bainite or ausferrite. [5] Tempering adds another stage and thus cost to the process; it does not provide the same property modification and stress relief in Bainite or ausferrite that it does for virgin Martensite.
The high temperature of annealing may result in oxidation of the metal's surface, resulting in scale. If scale must be avoided, annealing is carried out in a special atmosphere, such as with endothermic gas (a mixture of carbon monoxide, hydrogen gas, and nitrogen gas). Annealing is also done in forming gas, a mixture of hydrogen and nitrogen.
Holloman and Jaffe determined the value of C experimentally by plotting hardness versus tempering time for a series of tempering temperatures of interest and interpolating the data to obtain the time necessary to yield a number of different hardness values. This work was based on six different heats of plain carbon steels with carbon contents ...
The rate of the microscopic mechanisms controlling the nucleation and growth of recrystallized grains depend on the annealing temperature. Arrhenius-type equations indicate an exponential relationship. Critical temperature. Following from the previous rule it is found that recrystallization requires a minimum temperature for the necessary ...