A 25% strength gain between 7 and 28 days is often observed with 100% OPC (ordinary Portland cement) mixtures, and between 25% and 40% strength gain can be realized with the inclusion of pozzolans such as flyash, and supplementary cementitious materials (SCMs) such as slag cement. Strength gain depends on the type of mixture, its constituents ...
As per Indian codes, compressive strength of concrete is defined as: Field cured concrete in cubic steel molds (Greece) The compressive strength of concrete is given in terms of the characteristic compressive strength of 150 mm size cubes tested after 28 days (fck). In field, compressive strength tests are also conducted at interim duration i.e ...
High-strength concrete has a compressive strength greater than 40 MPa (6000 psi). In the UK, BS EN 206-1 [2] defines High strength concrete as concrete with a compressive strength class higher than C50/60. High-strength concrete is made by lowering the water-cement (W/C) ratio to 0.35 or lower.
Young's modulus is the slope of the linear part of the stress–strain curve for a material under tension or compression.. Young's modulus (or Young modulus) is a mechanical property of solid materials that measures the tensile or compressive stiffness when the force is applied lengthwise.
Mechanical evaluation of the pozzolanic activity is based upon a comparison of the compressive strength of mortar bars containing pozzolans as a partial replacement for Portland cement to reference mortar bars containing only Portland cement as binder. The mortar bars are prepared, cast, cured and tested following a detailed set of prescriptions.
The creep of concrete, which originates from the calcium silicate hydrates (C-S-H) in the hardened Portland cement paste (which is the binder of mineral aggregates), is fundamentally different from the creep of metals as well as polymers. Unlike the creep of metals, it occurs at all stress levels and, within the service stress range, is ...
Their addition allows to decrease the water-to-cement ratio of concrete or mortar without negatively affecting the workability of the mixture. It enables the production of self-consolidating concrete and high-performance concrete. The water–cement ratio is the main factor determining the concrete strength and its durability. Superplasticizers ...
Gypsum concrete is lightweight and fire-resistant. A 1.5-inch slab of gypsum concrete weighs 13 pounds per square foot versus 18 pounds per square foot for regular concrete. [10] Even though gypsum concrete weighs less, it still has the same compressive strength as regular concrete, based on its application as underlayment or top coat flooring ...