Alite is an impure form of tricalcium silicate, Ca 3 SiO 5, sometimes formulated as 3CaO·SiO 2 (C 3 S in cement chemist notation), typically with 3-4% of substituent oxides. [1] It is the major, and characteristic, phase in Portland cement.
It is a shorthand way of writing the chemical formula of oxides of calcium, silicon, ... Tricalcium silicate: Alite: C 2 S: 2 CaO · SiO 2: Dicalcium silicate: Belite ...
Calcium-silicate passive fire protection board being clad around steel structure in order to achieve a fire-resistance rating. Calcium silicate is commonly used as a safe alternative to asbestos for high-temperature insulation materials. Industrial-grade piping and equipment insulation is often fabricated from calcium silicate.
Cement hydration and strength development mainly depend on two silicate phases: tricalcium silicate (C 3 S) , and dicalcium silicate (C 2 S) . [1] Upon hydration, the main reaction products are calcium silicate hydrates (C-S-H) and calcium hydroxide Ca(OH) 2, written as CH in the cement chemist notation. C-S-H is the phase playing the role of ...
Tricalcium silicate is responsible for most of the early strength (first 7 days). [3] Dicalcium silicate, which reacts more slowly, only contributes to late strength. Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water.
MTA is composed mostly of tricalcium silicate, dicalcium silicate, tricalcium aluminate, and tetracalcium aluminoferrite, with calcium sulfate and bismuth oxide as minor constituents. [3] The later 4 phases vary among the commercial products available.
C 3 A: tricalcium aluminate (3CaO·Al 2 O 3) (historically, and still occasionally, called celite); C 4 AF: brownmillerite (4CaO·Al 2 O 3 ·Fe 2 O 3 ). The silicates are responsible for the cement's mechanical properties — the tricalcium aluminate and brownmillerite are essential for the formation of the liquid phase during the sintering ...
Tricalcium aluminate Ca 3 Al 2 O 6, often formulated as 3CaO·Al 2 O 3 to highlight the proportions of the oxides from which it is made, is the most basic of the calcium aluminates. It does not occur in nature, but is an important mineral phase in Portland cement .