The energy consumed in manufacturing ductile iron pipe was 19.55 MJ per kg and volume of emissions released during manufacture was 1.430 kg CO 2 per kg, compared to 68.30 MJ per kg of energy and 4.860 kg CO 2 per kg emissions for PVC pipes, and 1.24 MJ per kg and 0.148 kg CO 2 per kg for concrete pipes of the same diameter.
Steel casing pipe is often specified as ASTM A-252 which is a structural grade material that does not require hydrostatic testing and the inspection requirements are not stringent and it usually costs less than other grades such as A-53, [2] A-139 or API 5L. Used natural gas line pipe is also used as casing on many projects because it is often ...
For example, NPS 2 inch and DN 50 are the same pipe, but the actual OD is 2.375 inches or 60.33 millimetres. The only way to obtain the actual OD is to look it up in a reference table. For pipe sizes of NPS 14 inch (DN 350) and greater the NPS size is the actual diameter in inches and the DN size is equal to NPS times 25 (not 25.4) rounded to a ...
While pipe sizes in Australia are inch-based, they are classified by outside rather than inside diameter (e.g., a nominal 3 ⁄ 4 inch copper pipe in Australia has measured diameters of 0.750 inches outside and 0.638 inches inside, whereas a nominal 3 ⁄ 4 inch copper pipe in the U.S. and Canada has measured diameters of 0.875 inch outside and ...
Nominal Pipe Size (NPS) is a North American set of standard sizes for pipes used for high or low pressures and temperatures. [1] " Nominal" refers to pipe in non-specific terms and identifies the diameter of the hole with a non-dimensional number (for example – 2-inch nominal steel pipe" consists of many varieties of steel pipe with the only criterion being a 2.375-inch (60.3 mm) outside ...
4. Materials and Manufacture of ASTM A53 Pipes 4.1 The steel for both seamless and welded pipe shall be made by one or more of the following processes: open-hearth, electric-furnace, or basic-oxygen. 4.2 If steels of different grades are sequentially strand cast, identification of the resultant transition material is required.