Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
SAE 316 stainless steel is a molybdenum-alloyed steel and the second most common austenitic stainless steel (after grade 304). It is the preferred steel for use in marine environments because of its greater resistance to pitting corrosion than most other grades of steel without molybdenum. [ 1 ]
To qualify as stainless steel, Fe-base alloys must contain at least 10.5%Cr. The iron-chromium phase diagram shows that up to about 13%Cr, the steel undergoes successive transformations upon cooling from the liquid phase from ferritic α phase to austenitic γ phase and back to α.
Stainless steel can pose special corrosion challenges, since its passivating behavior relies on the presence of a major alloying component (chromium, at least 11.5%). Because of the elevated temperatures of welding and heat treatment, chromium carbides can form in the grain boundaries of stainless alloys.
In general, crevice corrosion is of greatest concern for materials which are normally passive metals, like stainless steel or aluminum. Crevice corrosion tends to be of greatest significance to components built of highly corrosion-resistant superalloys and operating with the purest-available water chemistry.
304 stainless steel is also used in the architectural field for exterior accents such as water and fire features. It is also a common coil material for vaporizers. Early SpaceX Starships used SAE 301 stainless steel in their construction, [8] before moving over to SAE 304L for the SN7 test tank [broken anchor] [9] and Starship SN8 in 2020. [10]
Stainless steel, also known as "inox steel" does not stain, corrode, or rust as easily as ordinary steel. Pierre Berthier, a Frenchman, was the first to notice the rust-resistant properties of mixing chromium with alloys in 1821, which led to new metal treating and metallurgy processes, and eventually the creation of usable stainless steel.
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]