Both quantitative and qualitative tests for solderability exist. [6] The two most common testing methods are the 'dip and look' method and wetting balance analysis.In both of these tests, the soldered pieces undergo an accelerated aging process before being tested for solderability, to take into consideration the time a component was in storage prior to mounting to final assembly.
Solder, used to fuse metals such as pipes and electrical connections, is basically pewter wire. Solder has often a lower tin content than normal pewter (around 60% ...
Pewter (/ ˈ p juː t ər /) is a malleable metal alloy consisting of tin (85–99%), antimony (approximately 5–10%), copper (2%), bismuth, and sometimes silver. [1] In the past, it was an alloy of tin and lead , but most modern pewter, in order to prevent lead poisoning , is not made with lead.
An inexpensive alloy that is easily cast and worked, spelter was used from the 1860s in the manufacture of candlesticks, clock cases, tableware, and light fixtures. In the early 20th century, sculptors such as Jacques Limousin used spelter heavily in their manufacture of Art Nouveau and Art Deco figurines and other ornaments.
Wood's metal. Wood's metal, also known as Lipowitz's alloy or by the commercial names Cerrobend, Bendalloy, Pewtalloy and MCP 158, is a metal alloy that is useful for soldering and making custom metal parts, but its fumes are toxic, as well as being toxic on skin exposure.
Toy road roller cast from zinc. Pot metal (or monkey metal) is an alloy of low-melting point metals that manufacturers use to make fast, inexpensive castings. The term "pot metal" came about because of automobile factories' practice in the early 20th century of gathering up non-ferrous metal scraps from the manufacturing processes and melting them in one pot to form into cast products.
Britannia metal (also called britannium, Britannia ware, [1] or Vickers White Metal [2]) is a specific type of pewter alloy, favoured for its silvery appearance and smooth surface. The composition by weight is typically about 92–93% tin , 5–6% antimony , and 2% copper .
Gray for tin or pewter. Use 20% aqueous solution of ferric chloride, it is necessary to immerse the objects in solution, dry and wax or varnish. [30] Gray-black for zinc. Use 20% aqueous solution of ferric chloride, the objects are immersed for 20 minutes, after the appearance of colour, objects should be washed, dried and waxed or varnished. [30]