This block is one of three displacements, 302/327/350, that underwent a crankshaft bearing diameter transformation for 1968 when the rod-journal size was increased from the 2 in (50.8 mm) diameter small-journal to a 2.1 in (53.3 mm) large-journal and a main-journal size that was increased from 2.3 in (58.4 mm) to 2.45 in (62.2 mm).
Ceramic mold casting, also known ambiguously as ceramic molding, [1] is a group of metal casting processes that use ceramics as the mold material. It is a combination of plaster mold casting and investment casting. [2] [3] There are two types of ceramic mold casting: the Shaw process and the Unicast process. [4]
Permanent mold casting is a metal casting process that employs reusable molds ("permanent molds"), usually made from metal. The most common process uses gravity to fill the mold. However, gas pressure or a vacuum are also used. A variation on the typical gravity casting process, called slush casting, produces hollow castings.
Typical products made using this process are television tubes and missile nose cones. [citation needed] Spin casting is also used to manufacture large telescope mirrors, where the natural curve followed by the molten glass greatly reduces the amount of grinding required. Rather than pouring glass into a mold an entire turntable containing the ...
The process can be used for both small castings of a few ounces and large castings weighing several hundred pounds. However, it is most suitable for small parts at large volumes. [5] It can be more expensive than die casting or sand casting, but per-unit costs decrease with large volumes. Investment casting can produce complicated shapes that ...
Evaporative-pattern casting is a type of casting process that uses a pattern made from a material that will evaporate when the molten metal is poured into the molding cavity. The most common evaporative-pattern material used is polystyrene foam. [1] The two major evaporative-pattern casting processes are: [1] Lost-foam casting; Full-mold casting
Like sand casting, plaster mold casting is an expendable mold process, however it can only be used with non-ferrous materials. It is used for castings as small as 30 g (1 oz) to as large as 7–10 kg (15–22 lb). Generally, the form takes less than a week to prepare. Production rates of 1–10 units/hr can be achieved with plaster molds. [1] [2]
Lost-foam casting (LFC) is a type of evaporative-pattern casting process that is similar to investment casting except foam is used for the pattern instead of wax. This process takes advantage of the low boiling point of polymer foams to simplify the investment casting process by removing the need to melt the wax out of the mold.