Accelerated curing is any method by which high early age strength is achieved in concrete. These techniques are especially useful in the prefabrication industry, wherein high early age strength enables the removal of the formwork within 24 hours, thereby reducing the cycle time, resulting in cost-saving benefits. [ 1 ]
During the curing period, concrete is ideally maintained at controlled temperature and humidity. To ensure full hydration during curing, concrete slabs are often sprayed with "curing compounds" that create a water-retaining film over the concrete. Typical films are made of wax or related hydrophobic compounds.
Cracks due to a poor curing (loss of water at early age) The curing of concrete when it continues to harden after its initial setting and progressively develops its mechanical strength is a critical phase to avoid unwanted cracks in concrete.
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
Self-drying concrete technology is found in certain cementitious patching and leveling materials and tile-setting mortars used in the flooring industry. Self-drying technology allows the cement mix to consume all of its mix water while curing, eliminating the need for excess water to evaporate prior to installing flooring.
Weathering carbonation occurs in concrete when calcium compounds react with carbon dioxide (CO 2) from the atmosphere and water (H 2 O) in the concrete pores. The reaction is as follows. First, through chemical weathering, CO 2 reacts with water in the concrete pores to form carbonic acid: CO 2 + H 2 O ⇌ H 2 CO 3
Their addition allows to decrease the water-to-cement ratio of concrete or mortar without negatively affecting the workability of the mixture. It enables the production of self-consolidating concrete and high-performance concrete. The water–cement ratio is the main factor determining the concrete strength and its durability. Superplasticizers ...
The concrete at young age must be protected against water evaporation due to direct insolation, elevated temperature, low relative humidity and wind. The interfacial transition zone (ITZ) is a region of the cement paste around the aggregate particles in concrete. In the zone, a gradual transition in the microstructural features occurs. [52]