The tablet is pushed against a stationary anvil until it fractures. A reading is taken from a scale indicator. [5] Kraemer Elektronik's tablet testing system was the first automatic tablet hardness testing system for auto-regulation at tablet presses, invented by German mechanical engineer Mr. Norbert Kraemer in Darmstadt, Germany.
Friability testing is a laboratory technique used by the pharmaceutical industry to test the durability of tablets during transit. This testing involves repeatedly dropping a sample of tablets over a fixed time, using a rotating wheel with a baffle. The result is inspected for broken tablets, and the percentage of tablet mass lost through ...
Tablet hardness testing; Turner-sclerometer; V. Vickers hardness test This page was last edited on 16 March 2013, at 18:53 (UTC). Text is available under the ...
The physical properties of a tablet are tested either by manual or automated sampling and IPC testing (in-process control). Tablet "hardness", also called "breaking force", is tested to assure that the tablet's strength will survive all further processes, such as dedusting, coating and packaging.
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .
The governing standard for the Barcol hardness test is ASTM D 2583. [4] Barcol hardness is measured on a scale from 0 to 100 with the typical range being between 50B and 90B. A measurement of 60B is roughly equivalent to a Shore hardness of 80D or a Rockwell hardness M100.
Meyer's law is often used to relate hardness values based on the fact that if the weight is quartered, the diameter of the indenter is halved. For instance, the hardness values are the same for a test load of 3000 kgf with a 10 mm indenter and for a test load of 750 kgf with a 5 mm diameter indenter.
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...