An example batch calculation may be demonstrated here. The desired glass composition in wt% is: 67 SiO 2, 12 Na 2 O, 10 CaO, 5 Al 2 O 3, 1 K 2 O, 2 MgO, 3 B 2 O 3, and as raw materials are used sand, trona, lime, albite, orthoclase, dolomite, and borax.
The structure of sodium oxide has been determined by X-ray crystallography.Most alkali metal oxides M 2 O (M = Li, Na, K, Rb) crystallise in the antifluorite structure.In this motif the positions of the anions and cations are reversed relative to their positions in CaF 2, with sodium ions tetrahedrally coordinated to 4 oxide ions and oxide cubically coordinated to 8 sodium ions.
In industry, the various grades of sodium silicate are characterized by their SiO 2:Na 2 O weight ratio (which can be converted to molar ratio by multiplication with 1.032). The ratio can vary between 1:2 and 3.75:1. [1]
Sodium peroxide is an inorganic compound with the formula Na 2 O 2.This yellowish solid is the product of sodium ignited in excess oxygen. [3] It is a strong base. This metal peroxide exists in several hydrates and peroxyhydrates including Na 2 O 2 ·2H 2 O 2 ·4H 2 O, Na 2 O 2 ·2H 2 O, Na 2 O 2 ·2H 2 O 2, and Na 2 O 2 ·8H 2 O. [4] The octahydrate, which is simple to prepare, is white, in ...
A hot water solution containing 73.1% (mass) of NaOH is a eutectic that solidifies at about 62.63 °C as an intimate mix of anhydrous and monohydrate crystals. [ 21 ] [ 20 ] A second stable eutectic composition is 45.4% (mass) of NaOH, that solidifies at about 4.9 °C into a mixture of crystals of the dihydrate and of the 3.5-hydrate.
Equivalent weights may be calculated from molar masses if the chemistry of the substance is well known: sulfuric acid has a molar mass of 98.078(5) g mol −1, and supplies two moles of hydrogen ions per mole of sulfuric acid, so its equivalent weight is 98.078(5) g mol −1 /2 eq mol −1 = 49.039(3) g eq −1.
Diagram of Castner process apparatus. The Castner process is a process for manufacturing sodium metal by electrolysis of molten sodium hydroxide at approximately 330 °C. Below that temperature, the melt would solidify; above that temperature, the molten sodium would start to dissolve in the melt.
The molar mass of a substance depends not only on its molecular formula, but also on the distribution of isotopes of each chemical element present in it. For example, the molar mass of calcium-40 is 39.962 590 98 (22) g/mol, whereas the molar mass of calcium-42 is 41.958 618 01 (27) g/mol, and of calcium with the normal isotopic mix is 40.078(4 ...