Line defects can be described by gauge theories. Dislocations are linear defects, around which the atoms of the crystal lattice are misaligned. [14] There are two basic types of dislocations, the edge dislocation and the screw dislocation. "Mixed" dislocations, combining aspects of both types, are also common. An edge dislocation is shown. The ...
Schematic diagram (lattice planes) showing an edge dislocation. Burgers vector in black, dislocation line in blue. A crystalline material consists of a regular array of atoms, arranged into lattice planes. An edge dislocation is a defect where an extra half-plane of atoms is introduced midway through the crystal, distorting nearby planes of atoms.
PSB structure (adopted from [7]). Persistent slip-bands (PSBs) are associated with strain localisation due to fatigue in metals and cracking on the same plane. Transmission electron microscopy (TEM) and three-dimensional discrete dislocation dynamics (DDD [8]) simulation were used to reveal and understand dislocations type and arrangement/patterns to relate it to the sub-surface structure.
In other cases, the dislocations may interact to form a more complex hexagonal structure. These concepts of tilt and twist boundaries represent somewhat idealized cases. The majority of boundaries are of a mixed type, containing dislocations of different types and Burgers vectors, in order to create the best fit between the neighboring grains.
The vector's magnitude and direction is best understood when the dislocation-bearing crystal structure is first visualized without the dislocation, that is, the perfect crystal structure. In this perfect crystal structure, a rectangle whose lengths and widths are integer multiples of a (the unit cell edge length) is drawn encompassing the site ...
Splitting into two partial dislocations is favorable because the energy of a line defect is proportional to the square of the burger’s vector magnitude. For example, an edge dislocation may split into two Shockley partial dislocations with burger’s vector of 1/6<112>. [4] This direction is no longer in the closest packed direction, and ...
Dislocation glide cannot act on its own to produce large strains due to the effects of strain-hardening, where a dislocation ‘tangle’ can inhibit the movement of other dislocations, which then pile up behind the blocked ones causing the crystal to become difficult to deform. Diffusion and dislocation creep can occur simultaneously.
In crystallography, a vacancy is a type of point defect in a crystal where an atom is missing from one of the lattice sites. [2] Crystals inherently possess imperfections, sometimes referred to as crystallographic defects. Vacancies occur naturally in all crystalline materials.