Cold cracking—also known as delayed cracking, hydrogen-assisted cracking (HAC), or hydrogen-induced cracking (HIC)—is a type of defect that often develops after solidification of the weld when the temperature starts to drop from about 190 °C (375 °F); the phenomenon often arises at room temperature, and it can take up to 24 hours to appear even after complete cooling. [8]
In welding, undercutting is when the weld reduces the cross-sectional thickness of the base metal. This type of defect reduces the strength of the weld and workpieces. One reason for this defect is excessive current, causing the edges of the joint to melt and drain into the weld; this leaves a drain-like impression along the length of the weld.
Engineering Critical Assessment (ECA) is a procedure by which the safety of a welded structure with defects or flaws can be determined. ECAs utilize the material properties and expected stress history to determine a flaw acceptance criteria which will ensure that welds will not fail during the construction or service life of the welded structure. [1]
Solid-state welding processes classification chart [49] Like forge welding ... Types of welding defects include cracks, distortion, gas inclusions (porosity), ...
Weld defects such as misalignment, porosity, lack of fusion and degradation of the matrix and/or fibers may be visually apparent. Subsurface defects may not be visible, unless the composite matrix was nearly transparent and the embedded fibers did not obscure them. [6] Ultrasonic A-scan display showing a reflector in the part being tested.
Welding - Studs and ceramic ferrules for arc stud welding: ISO 13919-1: Welding - Electron and laser-beam welded joints - Guidance on quality level for imperfections - Part 1: Steel ISO 13919-2: Welding - Electron and laser-beam welded joints - Guidance on quality level for imperfections - Part 2: Aluminium and its weldable alloys ISO 13920
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Most weld purging is carried out on joints made by the TIG or GTAW arc welding process. [6] When the laser welding process is chosen, joints or welds being made on reactive materials will need to be carried out and in the case of electron beam welding, this is carried out in a vacuum, in which case purging takes place by complete evacuation of all gas.