2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and a maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]
Aluminum: 97.3 Silicon: 1 Magnesium: 0.80 Manganese: 0.5 Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa ... on 27 April 2024, ...
Print/export Download as PDF ... Shear strength 62 MPa Elastic modulus ... 0.33 Thermal conductivity 227 W/mK Ultimate Tensile Strength 75 MPa [2] Designations. 7072 ...
It has high toughness, high strength. It has high stress corrosion cracking resistance. [1] It has electric conductivity of value having 40 percent of copper. [2] 7050 aluminium is known as a commercial aerospace alloy. [3]
At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si. At room temperature, silicon is practically insoluble. Aluminum cannot be dissolved in silicon at all, not even at high temperatures. Only in the molten state are both completely soluble. Increases in strength due to solid solution strengthening are negligible. [7]
5456 aluminium–magnesium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). While it is closely related to 5356 aluminium alloy (Aluminum Association designations that only differ in the second digit are variations on the same alloy), it is used in structural applications, like most other aluminium-magnesium alloys, and not as filler for welding.
7055: High-Strength Plate and Extrusion Alloy Microstructure characterization of 7055-T6, 6061-T6511 and 7A52-T6 Al alloys subjected to ballistic impact against heavy tungsten alloy projectile Grain size prediction and investigation of 7055 aluminum alloy inoculated by Al–5Ti–1B master alloy,Journal of Alloys and Compounds - X-MOL