Welded aluminium alloy bicycle frame, made in the 1990s. An aluminium alloy (UK/IUPAC) or aluminum alloy (NA; see spelling differences) is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper, magnesium, manganese, silicon, tin, nickel and zinc.
6063 is the most common alloy used for aluminium extrusion. It allows complex shapes to be formed with very smooth surfaces fit for anodizing and is popular for visible architectural applications such as window frames, door frames, roofs, and sign frames. [3] Applications requiring higher strength typically use 6061 or 6082 instead.
6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. [ 2 ]
The yield strength of pure aluminium is 7–11 MPa, while aluminium alloys have yield strengths ranging from 200 MPa to 600 MPa. [32] Aluminium is ductile , with a percent elongation of 50–70%, [ 33 ] and malleable allowing it to be easily drawn and extruded . [ 34 ]
7075 aluminium alloy ... As is the case for all 7075 aluminum alloys, 7075-0 is highly corrosion-resistant combined with generally acceptable strength profile ...
5 Aluminum alloy table. ... 1200 Aluminium alloy has aluminium as the major element, and has silicon, ... Fatigue strength: 49 MPa U.T.S. 130 MPa
Aluminium-silicon alloys typically contain 3% to 25% silicon content. [1] Casting is the primary use of aluminum-silicon alloys, but they can also be utilized in rapid solidification processes and powder metallurgy. Alloys used by powder metallurgy, rather than casting, may contain even more silicon, up to 50%. [1]
6005A aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is closely related, but not identical, to 6005 aluminium alloy . Between those two alloys, 6005A is more heavily alloyed, but the difference does not make a marked impact on material properties.