Xylan is generally used to reduce friction, improve wear resistance, and for non-stick applications. Additionally, it can be used to protect a metal from corrosion.The most commonly known application is in non-stick cookware but Xylan coatings have also been used extensively in the automotive industry and for corrosion protection in the oil and gas industry.
Anti-friction (AF) coatings are "lubricating paints" consisting of fine particles of lubricating pigments, such as molydisulfide, PTFE or graphite, blended with a binder. After application and proper curing, these "slippery" or dry lubricants bond to the metal surface and form a dark gray solid film.
Solid film lubricants are paint-like coatings of very fine particles of lubricating pigment blended with a binder and other additives. The lubricant is applied to a substrate by spray, dip or brush methods and, once cured, creates a solid film which repels water, reduces friction and increases the wear life of the substrate to which it has been applied. [1]
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
A phosphate coating is usually obtained by applying to the steel part a dilute solution of phosphoric acid, possibly with soluble iron, zinc, and/or manganese salts. The solution may be applied by sponging, spraying, or immersion. [6] Phosphate conversion coatings can also be used on aluminium, zinc, cadmium, silver and tin. [7] [8]
PVD is used to enhance the wear resistance of steel cutting tools' surfaces and decrease the risk of adhesion and sticking between tools and a workpiece. This includes tools used in metalworking or plastic injection molding. [11]: 2 The coating is typically a thin ceramic layer less than 4 μm that has very high hardness and low friction. It is ...
Because electrolytically zinc-plated surfaces provide comparatively little corrosion protection, and in the case of galvanic zinc coatings on high-strength steel (e.g. category 10.9 and 12.9 high-strength bolts) there is a risk of hydrogen embrittlement, the industry needed a better corrosion protection system.
Chameleon coatings are also often used on hypersonic and reusable launch vehicles that require lubrication in ambient atmosphere, vacuum , and during re-entry (high temperature). A typical multilayer coating may use a molybdenum disulfide or diamond-like carbon for low friction at ambient conditions.