The chromate coating acts as paint does, protecting the zinc from white corrosion, thus making the part considerably more durable, depending on the chromate layer's thickness. [8] [9] [10] The protective effect of chromate coatings on zinc is indicated by color, progressing from clear/blue to yellow, gold, olive drab and black.
Anodizing increases resistance to corrosion and wear, and provides better adhesion for paint primers and glues than bare metal does. Anodic films can also be used for several cosmetic effects, either with thick porous coatings that can absorb dyes or with thin transparent coatings that add reflected light wave interference effects.
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound.
It is far cheaper than similar corrosion protection systems, such as paint and electroplating. The oldest and most widely used specification for hot black oxide is MIL-DTL-13924, which covers four classes of processes for different substrates. Alternate specifications include AMS 2485, ASTM D769, and ISO 11408. [citation needed]
Black for aluminum. Boil a solution of 20 g ammonium molybdate and 5 g of sodium thiosulfate in a liter of water, immerse the objects, rinse, dry, wax or lacquer after the development of color. [31] Lustre colours. Use a solution of 280 g of sodium thiosulphate, 25 g of cupric acetate and 30 g of citric acid. It can be used on copper and its ...