To obtain functional joints, the inside of the fitting and the outside of the copper pipe are cleaned using steel wool or cleaning tape, flux paste is applied, the pipe is inserted into the fitting and heat is applied from a portable butane torch or propane torch until a ring of solder shows at the edges of the fitting. To obtain a durable ...
For example, DN20 is the size for copper pipe with an outside diameter of 19.05 mm or 3 ⁄ 4 inch. While pipe sizes in Australia are inch-based, they are classified by outside rather than inside diameter (e.g., a nominal 3 ⁄ 4 inch copper pipe in Australia has measured diameters of 0.750 inches outside and 0.638 inches inside, whereas a ...
The welding of metals differs from soldering and brazing in that the joint is made without adding a lower-melting-point material (e.g. solder); instead, the pipe or tubing material is partially melted, and the fitting and piping are directly fused. This generally requires piping and fitting to be the same (or compatible) material.
Pipe sizes can be confusing because the terminology may relate to historical dimensions. For example, a half-inch iron pipe does not have any dimension that is a half inch. Initially, a half inch pipe did have an inner diameter of 1 ⁄ 2 inch (13 mm)—but it also had thick walls. As technology improved, thinner walls became possible, but the ...
Rosin used as flux for soldering A flux pen used for electronics rework Multicore solder containing flux Wire freshly coated with solder, held above molten rosin flux. In metallurgy, a flux is a chemical reducing agent, flowing agent, or purifying agent. Fluxes may have more than one function at a time.
Copper to lead joints may be made by wiping the lead onto the copper pipe, as for a lead-lead joint. However the Pb 80 Sn 20 solder used for wiping is poorly wetting onto copper, and so that must be tinned first, using a more tin-rich solder and an active flux.