A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
number symbol name Mohs hardness [1] Vickers hardness (MPa) [1] Brinell hardness (MPa) [1] Brinell hardness (MPa) [note 1] [2] 3: Li: lithium: 0.6: 5: 4: Be: beryllium: 5.5: 1670: 590–1320: 5: B: boron
ASTM D2240 durometers allow for a measurement of the initial hardness, or the indentation hardness after a given period of time. The basic test requires applying the force in a consistent manner, without shock, and measuring the hardness (depth of the indentation). If a timed hardness is desired, force is applied for the required time and then ...
The hardness of abrasion resistant steel is determined by a Brinell hardness test. This test uses a small steel ball to inflict force on a material. The indentation created by the steel ball is then measured and used to calculate Brinell hardness number (BHN).
Brinelling / ˈ b r ɪ n ə l ɪ ŋ / is the permanent indentation of a hard surface. It is named after the Brinell scale of hardness, in which a small ball is pushed against a hard surface at a preset level of force, and the depth and diameter of the mark indicates the Brinell hardness of the surface.
For annealed materials the Meyer hardness increases continuously with load due to strain hardening. [2] Based on Meyer's law hardness values from this test can be converted into Brinell hardness values, and vice versa. [3] The Meyer hardness test was devised by Eugene Meyer of the Materials Testing Laboratory at the Imperial School of ...
By comparison, a Brinell indentation on the same material is ~3 mm (hardness value ~400 HBW 10/3000), with a standard-compliant measuring time of ~15 seconds plus the time for measuring the indentation.