Titanium alloys make lightweight products like pocketknives Grade 1 is the most ductile and softest titanium alloy. It is a good solution for cold forming and corrosive environments. ASTM/ASME SB-265 provides the standards for commercially pure titanium sheet and plate. [18] Grade 2 Unalloyed titanium, standard oxygen. Grade 2H
Titanium Beta C refers to Ti Beta-C, a trademark for an alloy of titanium originally filed by RTI International. [1] It is a metastable "beta alloy" which was originally developed in the 1960s; Ti-3Al-8V-6Cr-4Mo-4Zr, nominally 3% aluminum , 8% vanadium , 6% chromium , 4% molybdenum , 4% zirconium and balance (75%): titanium .
Ti-6Al-4V titanium alloy commonly exists in alpha, with hcp crystal structure, (SG : P63/mmc) and beta, with bcc crystal structure, (SG : Im-3m) phases. While mechanical properties are a function of the heat treatment condition of the alloy and can vary based upon properties, typical property ranges for well-processed Ti-6Al-4V are shown below.
The ATI 425 Titanium Alloy is a titanium alloy developed and produced by Allegheny Technologies Incorporated (ATI). It is produced in multiple product forms, including sheet, coil, strip, Precision Rolled Strip and foil, plate, seamless tube, shapes and rectangles, as well as castings.
In the direct powder rolling (DPR) process BE powder is used to produce sheet and plate and composite multilayered sheet and plates. Sheets between 1.27 and 2.54 mm and 50 to 99+% dense of single layer CP titanium, Ti Grade 5, TiAl (Ti-48Al-2Cr-2Nb) and composite Ti/Grade 5/Ti and Grade 5/TiAl/Grade 5 have been produced by DPR and sintering.
A titanium cylinder of quality "grade 2" Titanium is used in steel as an alloying element (ferro-titanium) to reduce grain size and as a deoxidizer, and in stainless steel to reduce carbon content. [11] Titanium is often alloyed with aluminium (to refine grain size), vanadium, copper (to harden), iron, manganese, molybdenum, and other metals. [96]
High-strength low-alloy steel (HSLA) is a type of alloy steel that provides better mechanical properties or greater resistance to corrosion than carbon steel. HSLA steels vary from other steels in that they are not made to meet a specific chemical composition but rather specific mechanical properties.
Ti-6Al-7Nb (UNS designation R56700) is an alpha-beta titanium alloy first synthesized in 1977 containing 6% aluminum and 7% niobium. It features high strength and has similar properties as the cytotoxic vanadium containing alloy Ti-6Al-4V. Ti-6Al-7Nb is used as a material for hip prostheses. [1]