Rust bluing was developed between hot and cold bluing processes, and was originally used by gunsmiths in the 19th century to blue firearms prior to the development of hot bluing processes. The process was to coat the gun parts in an acid solution, let the parts rust uniformly, then immerse the parts in boiling water to convert the red oxide Fe 2 O
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting.
Quench polish quench (QPQ) is a specialized type of nitrocarburizing case hardening that increases corrosion resistance. It is sometimes known by the brand name of Tufftride, Tenifer or Melonite. [1] Three steps are involved: nitrocarburize ("quench"), polish, and post-oxidize ("quench"). [2]
Polishing lines will be soft and less reflective than a #4 architectural finish. #7 Finish. A #7 finish is produced by polishing with a 280–320 grit belt or wheel and sisal buffing with a cut and color compound. This is a semi-bright finish that will still have some polishing lines but they will be very dull.
Concrete floor polished with 1800 grit. Polished concrete is a multi-step process where a concrete floor is mechanically ground, honed and polished with bonded abrasives in order to achieve a desired level of sheen or gloss. The Concrete Polishing Process. Concrete polishing begins with floor preparation. During this process, the floor is ...
The NaOH (caustic soda) and elevated temperature cause Fe 3 O 4 (black oxide) to form on the surface of the metal instead of Fe 2 O 3 (red oxide; rust). While it is physically denser than red oxide, the fresh black oxide is porous, so oil is then applied as post treatment to the heated part, which seals it by "sinking" into it.