Bainite is a plate-like microstructure that forms in steels at temperatures of 125–550 °C (depending on alloy content). [1] First described by E. S. Davenport and Edgar Bain, [2] [3] it is one of the products that may form when austenite (the face-centered cubic crystal structure of iron) is cooled past a temperature where it is no longer thermodynamically stable with respect to ferrite ...
Austempering is heat treatment that is applied to ferrous metals, most notably steel and ductile iron. In steel it produces a bainite microstructure whereas in cast irons it produces a structure of acicular ferrite and high carbon, stabilized austenite known as ausferrite. It is primarily used to improve mechanical properties or reduce ...
As a result of the transformation, the microconstituents, pearlite and bainite, form; pearlite forms at higher temperatures and bainite at lower. TTT diagram of isothermal transformations of a hypoeutectoid carbon steel; showing the main components obtained when cooling the steel and its relation with the Fe-C phase diagram of carbon steels.
Steel that has been heated above its upper critical temperature and then cooled in standing air is called normalized steel. Normalized steel consists of pearlite, martensite, and sometimes bainite grains, mixed together within the microstructure. This produces steel that is much stronger than full-annealed steel, and much tougher than tempered ...
Mild steel (carbon steel with up to about 0.2 wt% C) consists mostly of α-Fe and increasing amounts of cementite (Fe 3 C, an iron carbide). The mixture adopts a lamellar structure called pearlite . Since bainite and pearlite each contain α-Fe as a component, any iron-carbon alloy will contain some amount of α-Fe if it is allowed to reach ...
The properties of steel depend on its microstructure: the arrangement of different phases, some harder, some with greater ductility. At the atomic level, the four phases of auto steel include martensite (the hardest yet most brittle), bainite (less hard), ferrite (more ductile), and austenite (the most ductile). The phases are arranged by ...
Discover the latest breaking news in the U.S. and around the world — politics, weather, entertainment, lifestyle, finance, sports and much more.
The carbon diffusion during the formation of pearlite, just ahead of the growth front, is critical in determining the thickness of the lamellae and, consequently, the strength of the steel. [5] Bainite is a similar structure with lamellae much smaller than the wavelength of visible light and thus lacks this pearlescent appearance. It is ...