Porcelain tiles or ceramic tiles are either tiles made of porcelain, or relatively tough ceramic tiles made with a variety of materials and methods, that are suitable for use as floor tiles, or for walls. They have a low water absorption rate, generally less than 0.5 percent. The clay used to build porcelain tiles is generally denser than ...
The most important condition relates to ceramic chemical composition. If the silica and alumina ratio with low basic materials such as sodium and calcium is adjusted, the needle shape mullite forms at about 1400 °C and the needles will interlock. This mechanical interlocking contributes to the high mechanical strength of porcelain. [13] [14]
Bullnose ceramic tile trim Bullnose is a term used in building construction for rounded convex trim, particularly in masonry and ceramic tile . [ 1 ] It is also used in relation to road safety and (formerly) railroad engineering design.
Crazing is a spider web pattern of cracks penetrating the glaze. It is caused by tensile stresses greater than the glaze is able to withstand. [1] [2] Common reasons for such stresses are: a mismatch between the thermal expansions of glaze and body; from moisture expansion of the body; and in the case of glazed tiles fixed to a wall, movement of the wall or of the bonding material used to fix ...
The ISO 13006 defines a "porcelain tile" as a "fully vitrified tile with water absorption less than or equal to 0.5%, belonging to groups AIa and BIa (of ISO 13006).". [19] The ANSI defines as "a ceramic tile that has 'a water absorption of 0.5%' or less.” It is made generally by the pressed or extruded method."
The pattern appears inlaid into the body of the tile, so that the design remains as the tile is worn down. Encaustic tiles may be glazed or unglazed and the inlay may be as shallow as 1 ⁄ 8 inch (3 mm), as is often the case with "printed" encaustic tile from the later medieval period, or as deep as 1 ⁄ 4 in (6.4 mm).
A group of hydrous aluminium phyllosilicate minerals. Often also used to refer to the clay body, which sometimes may only contain small amounts of clay minerals. Clay body The material used to form an article of pottery. Thus a potter might prepare, or order from a supplier, such an amount of earthenware body, stoneware body or porcelain body ...
These are the cheapest range of bought materials and can be glazed or unglazed. The glazed ceramic tiles have the color painted onto the top of the clay and then fired to a high temperature in a kiln. The unglazed or body glazed version has the color mixed into the wet clay so the color runs through them. They vary in size. [2]