A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion, to improve the adherence of other coatings, for lubrication, or for aesthetic ...
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
Black oxide or blackening is a conversion coating for ferrous materials, stainless steel, copper and copper based alloys, zinc, powdered metals, and silver solder. [1] It is used to add mild corrosion resistance, for appearance, and to minimize light reflection. [2]
The reason for combining the processes can vary, however, the significant difference between anodizing and chromate conversion coating is the electrical conductivity of the films produced. Although both stable compounds, chromate conversion coating has a greatly increased electrical conductivity.
Rust converters are chemical solutions or primers that can be applied directly to an iron or iron alloy surface to convert iron oxides into a protective chemical barrier.
All blued parts still require oiling to prevent rust. Bluing, being a chemical conversion coating, is not as robust against wear and corrosion resistance as plated coatings, and is typically no thicker than 2.5 micrometres (0.0001 inches). For this reason, it is considered not to add any appreciable thickness to precisely-machined parts.
Aluminium chromate conversion coatings are amorphous in structure with a gel-like composition hydrated with water. [18] Chromate conversion is a common way of passivating not only aluminium, but also zinc, cadmium, copper, silver, magnesium, and tin alloys. Anodizing is an electrolytic process that forms a thicker oxide layer.