Glass wool, which is one product called "fiberglass" today, was invented some time between 1932 and 1933 by Games Slayter of Owens-Illinois, as a material to be used as thermal building insulation. [1] It is marketed under the trade name Fiberglas, which has become a genericized trademark. Glass fiber, when used as a thermal insulating material ...
Glass fibers have been produced for centuries, but the earliest patent was awarded to the Prussian inventor Hermann Hammesfahr (1845–1914) in the U.S. in 1880. [3] [4]Mass production of glass strands was accidentally discovered in 1932 when Games Slayter, a researcher at Owens-Illinois, directed a jet of compressed air at a stream of molten glass and produced fibers.
FR-4 is a composite material composed of woven fiberglass cloth with an epoxy resin binder that is flame resistant (self-extinguishing). "FR" stands for "flame retardant", and does not denote that the material complies with the standard UL94V-0 unless testing is performed to UL 94, Vertical Flame testing in Section 8 at a compliant lab.
Unless stated otherwise, the properties of fused silica (quartz glass) and germania glass are derived from the SciGlass glass database by forming the arithmetic mean of all the experimental values from different authors (in general more than 10 independent sources for quartz glass and T g of germanium oxide glass). The list is not exhaustive.
Density system unit unit-code symbol or abbrev. notes sample default conversion combination output units Metric: kilogram per cubic metre: kg/m3 kg/m 3: 1.0 kg/m 3 (1.7 lb/cu yd)
The specific weight, also known as the unit weight (symbol γ, the Greek letter gamma), is a volume-specific quantity defined as the weight W divided by the volume V of a material: = / Equivalently, it may also be formulated as the product of density, ρ, and gravity acceleration, g: = Its unit of measurement in the International System of Units (SI) is newton per cubic metre (N/m 3), with ...
(near r.t.) 1738 kg/m 3: LNG (at 20 °C) 1.738 g/cm 3: CRC (near r.t.) 1.74 g/cm 3: 13 Al aluminium; use: 2.70 g/cm 3: WEL (near r.t.) 2700 kg/m 3: LNG (at r.t.) 2.70 g/cm 3: CRC (near r.t.) 2.70 g/cm 3: 14 Si silicon; use: 2.33 g/cm 3: WEL (near r.t.) 2330 kg/m 3: LNG (at r.t.) 2.33 g/cm 3: CRC (near r.t.) 2.3290 g/cm 3: 15 P phosphorus (white ...
G-10 or garolite is a high-pressure fiberglass laminate, a type of composite material. [1] It is created by stacking multiple layers of glass cloth, soaked in epoxy resin, then compressing the resulting material under heat until the epoxy cures. [2] [3] It is manufactured in flat sheets, most often a few millimeters thick.