ZOE can be used as a dental filling material or dental cement in dentistry. [ 1 ] [ 2 ] It is often used in dentistry when the decay is very deep or very close to the nerve or pulp chamber. Because the tissue inside the tooth, i.e. the pulp , reacts badly to the drilling stimulus (heat and vibration), it frequently becomes severely inflamed and ...
Zinc phosphate was the very first dental cement to appear on the dental marketplace and is seen as the “standard” for other dental cements to be compared to. The many uses of this cement include permanent cementation of crowns, orthodontic appliances, intraoral splints, inlays, post systems, and fixed partial dentures.
A glass ionomer cement (GIC) is a dental restorative material used in dentistry as a filling material and luting cement, [1] including for orthodontic bracket attachment. [2] Glass-ionomer cements are based on the reaction of silicate glass-powder (calciumaluminofluorosilicate glass [ 3 ] ) and polyacrylic acid , an ionomer .
Mineral trioxide aggregate (MTA) is an alkaline, cementitious dental repair material. MTA is used for creating apical plugs during apexification, repairing root perforations during root canal therapy, and treating internal root resorption. It can be used for root-end filling material and as pulp capping material.
Indirect dental composites can be used for: Filling cavities in teeth, as fillings, inlays and/or onlays; Filling gaps (diastemas) between teeth using a shell-like veneer or; Reshaping of teeth; Full or partial crowns on single teeth; Bridges spanning 2-3 teeth; A stronger, tougher and more durable product is expected in principle.
If permanent restoration cannot be carried out immediately after tooth preparation, temporary restoration may be performed. The prepared tooth, ready for placement of restorative materials, is generally called a tooth preparation. Materials used may be gold, amalgam, dental composites, glass ionomer cement, or porcelain, among others.
They were introduced in the early 1990s as a hybrid of two other dental materials, dental composites and glass ionomer cement, in an effort to combine their desirable properties: aesthetics for dental composites (they are white and closely mimic tooth tissue, so can camouflage into a tooth very well) and the fluoride releasing ability for glass ...
The majority of clinical studies indicate the annual failure rates (AFRs) are between 1% and 3% with tooth colored fillings on back teeth. Root canaled (endodontically) treated teeth have AFRs between 2% and 12%. The main reasons for failure are cavities that occur around the filling and fracture of the real tooth.