440C (UNS designation S44004) is a martensitic 400 series stainless steel, [1] and has the highest carbon content of the 400 stainless steel series. It can be heat treated to reach hardness of 58 to 60 HRC. It can be used to make rolling contact stainless bearings, e.g. ball bearings and roller bearings. It is also used to make knife blades.
D2 is a high-carbon, high-chromium die steel and is the highest carbon alloy tool and die steel typically used in knife making. [ citation needed ] With a chrome content of 12%, some call it a "semi-stainless", because of the lack of free Chromium in solution, even though it is defined by ASM and ANSI as stainless, which contains at least 11.5% ...
Martensitic stainless steels can be high- or low-carbon steels built around the composition of iron, 12% up to 17% chromium, carbon from 0.10% (Type 410) up to 1.2% (Type 440C): [8] The chromium and carbon contents are balanced to have a martensitic structure.
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
The term hardened steel is often used for a medium or high carbon steel that has been given heat treatment and then quenching followed by tempering. The quenching results in the formation of metastable martensite, the fraction of which is reduced to the desired amount during tempering. This is the most common state for finished articles such as ...
Carbon steel is often divided into two main categories: low-carbon steel and high-carbon steel. It may also contain other elements, such as manganese, phosphorus, sulfur, and silicon, which can affect its properties. Carbon steel can be easily machined and welded, making it versatile for various applications.
This causes carbon to diffuse into the surface of the steel. The depth of this high carbon layer depends on the exposure time, but 0.5mm is a typical case depth. Once this has been done the steel must be heated and quenched to harden this higher carbon 'skin'. Below this skin, the steel core will remain soft due to its low carbon content.