Such zinc electroplating or zinc alloy electroplating maintains a dominant position among other electroplating process options, based upon electroplated tonnage per annum. According to the International Zinc Association, more than 5 million tons are used yearly for both hot-dip galvanization and electroplating. [ 1 ]
Galvanized surface with visible spangle. Galvanization (also spelled galvanisation) [1] is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc. [citation needed]
The process of hot-dip galvanizing results in a metallurgical bond between zinc and steel, with a series of distinct iron-zinc alloys. The resulting coated steel can be used in much the same way as uncoated. A typical hot-dip galvanizing line operates as follows: [2] Steel is cleaned using a caustic solution. This removes oil/grease, dirt, and ...
Mechanical plating, also known as peen plating, mechanical deposition, or impact plating, is a plating process that imparts the coating by cold welding fine metal particles to a workpiece. Mechanical galvanization is the same process, but applies to coatings that are thicker than 0.001 in (0.025 mm). [ 1 ]
A common example of galvanic corrosion occurs in galvanized iron, a sheet of iron or steel covered with a zinc coating. Even when the protective zinc coating is broken, the underlying steel is not attacked. Instead, the zinc is corroded because it is less "noble". Only after it has been consumed can rusting of the base metal occur.
Zinc is added to the soil primarily through the weathering of rocks, but humans have added zinc through fossil fuel combustion, mine waste, phosphate fertilizers, pesticide (zinc phosphide), limestone, manure, sewage sludge, and particles from galvanized surfaces. Excess zinc is toxic to plants, although zinc toxicity is far less widespread. [12]
Because electrolytically zinc-plated surfaces provide comparatively little corrosion protection, and in the case of galvanic zinc coatings on high-strength steel (e.g. category 10.9 and 12.9 high-strength bolts) there is a risk of hydrogen embrittlement, the industry needed a better corrosion protection system.
Production of galvannealed sheet steel begins with hot dip galvanization of sheet steel. After passing through the galvanizing zinc bath the sheet steel passes through air knives to remove excess zinc, and is then heated in an annealing furnace for several seconds causing iron and zinc layers to diffuse into one another causing the formation of zinc-iron alloy layers at the surface.