A standard black oxide is magnetite (Fe 3 O 4), which is more mechanically stable on the surface and provides better corrosion protection than red oxide Fe 2 O 3. Modern industrial approaches to forming black oxide include the hot and mid-temperature processes described below. Traditional methods are described in the article on bluing. They are ...
Rust converters are chemical solutions or primers that can be applied directly to an iron or iron alloy surface to convert iron oxides into a protective chemical barrier. These compounds interact with iron oxides, especially iron(III) oxide , converting them into an adherent black layer ( black oxide ) that is more resistant to moisture and ...
This method was adopted by larger firearm companies for large scale, more economical bluing. It does provide good rust resistance, which is improved with oil. "Rust bluing" and "fume bluing" provide the best rust and corrosion resistance as the process continually converts any metal that is capable of rusting into magnetite (Fe 3 O 4). Treating ...
Aluminium oxynitride (marketed under the name ALON by Surmet Corporation [3]) is a transparent ceramic composed of aluminium, oxygen and nitrogen.Aluminium oxynitride is optically transparent (≥80% for 2 mm thickness) in the near-ultraviolet, visible, and mid-wave-infrared regions of the electromagnetic spectrum.
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound.
Rust scale forming and flaking off from a steel bar heated to its forging temperature of 1200°C. Rapid oxidation occurs when heated steel is exposed to air. Rust is a general name for a complex of oxides and hydroxides of iron, [4] which occur when iron or some alloys that contain iron are exposed to oxygen and moisture for a long period of ...
Severe car body corrosion example. Rustproofing is the prevention or delay of rusting of iron and steel objects, or the permanent protection against corrosion.Typically, the protection is achieved by a process of surface finishing or treatment.
In the process of bluing, an oxidizing chemical reaction on an iron surface selectively forms magnetite (Fe 3 O 4), the black oxide of iron (as opposed to rust, the red oxide of iron (Fe 2 O 3)). Black oxide provides some protection against corrosion if also treated with a water-displacing oil to reduce wetting and galvanic action.