  2. 2024 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/2024_aluminium_alloy

    2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and a maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.

  3. 7068 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/7068_aluminium_alloy

    7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]

  4. 6010 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/6010_aluminium_alloy

    Aluminum: 97.3 Silicon: 1 Magnesium: 0.80 Manganese: 0.5 Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa ... on 27 April 2024, ...

  5. 7178 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/7178_aluminium_alloy

    7178 aluminum alloy is wrought alloy. ... Ultimate Tensile Strength [4] 607 MPa Tensile Yield Strength [4] ... This page was last edited on 6 June 2024, ...

  6. 7075 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/7075_aluminium_alloy

    T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [9] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.

  7. 7039 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/7039_aluminium_alloy

    "Properties of Wrought Aluminum and Aluminum Alloys: 7039", Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, Vol 2, ASM Handbook, ASM International, 1990, p. 109-111. Mechanical and ballistic properties of powder metal 7039 aluminium alloy joined by friction stir welding

  8. 7050 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/7050_aluminium_alloy

    Aluminium 7050 alloy is a heat treatable alloy. It has high toughness, high strength. It has high stress corrosion cracking resistance. [1] It has electric conductivity of value having 40 percent of copper. [2] 7050 aluminium is known as a commercial aerospace alloy. [3]

  9. 6061 aluminium alloy - Wikipedia

    en.wikipedia.org/wiki/6061_aluminium_alloy

    T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10]