Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
Pickling is a metal surface treatment used to remove impurities, such as stains, inorganic contaminants, and rust or scale from ferrous metals, copper, precious metals and aluminium alloys. [1] A solution called pickle liquor , which usually contains acid , is used to remove the surface impurities.
Various testing methods are available to determine the passivation (or passive state) of stainless steel. The most common methods for validating the passivity of a part is some combination of high humidity and heat for a period of time, intended to induce rusting. Electro-chemical testers can also be utilized to commercially verify passivation.
Various colors on stainless steel 18 Cr / 8 Ni 7.5 g of sodium dichromate , 1000 mL of sulfuric acid (1.24 g/cm 3 ), lead cathodes, object as an anode, 70-90 °C temp, 0,06 A/dm 2 , voltage 1.3 V – colors depend on the duration of the procedure (5-50 min.), brown, blue, reddish brown, yellow, green.
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
Nitinol biocompatibility is an important factor in biomedical applications.Nitinol (NiTi), which is formed by alloying nickel and titanium (~ 50% Ni), is a shape-memory alloy with superelastic properties more similar to that of bone, [clarification needed] when compared to stainless steel, another commonly used biomaterial.
Eco pickled surface (EPS) is a process applied to hot rolled sheet steel to remove all surface oxides and clean the steel surface.Steel which has undergone the EPS process acquires a high degree of resistance to subsequent development of surface oxide (rust), so long as it does not come into direct contact with moisture.
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...