Concrete creep is essentially the sagging of concrete over time. Creep and shrinkage of concrete are two physical properties of concrete.The creep of concrete, which originates from the calcium silicate hydrates (C-S-H) in the hardened Portland cement paste (which is the binder of mineral aggregates), is fundamentally different from the creep of metals and polymers.
After sufficient setting and hardening of concrete (after 28 days), the progressive loss of capillary water is also responsible for the "drying shrinkage". It is a continuous and long-term process occurring later during the concrete life when under dry conditions the larger pores of concrete are no longer completely saturated by water. Thermal ...
Concrete has a very low coefficient of thermal expansion, and as it matures concrete shrinks. All concrete structures will crack to some extent, due to shrinkage and tension. Concrete which is subjected to long-duration forces is prone to creep. The density of concrete varies, but is around 2,400 kilograms per cubic metre (150 lb/cu ft). [1]
Concrete is a composite material composed of aggregate bonded together with a fluid cement that cures to a solid over time. Concrete is the second-most-used substance in the world after water, [1] and is the most widely used building material. [2] Its usage worldwide, ton for ton, is twice that of steel, wood, plastics, and aluminium combined. [3]
The initiation time is related to the rate at which carbonation propagates in the concrete cover thickness.Once that carbonation reaches the steel surface, altering the local pH value of the environment, the protective thin film of oxides on the steel surface becomes instable, and corrosion initiates involving an extended portion of the steel surface.
Traditional concrete has a water:cement ratio of about 0.5, which refers to the weight of the water divided by the weight of the cement. A water:cement ratio of 0.5 provides good workability while keeping the amount of excess water in the mix fairly low. Without at least this much extra water, the concrete would be too dry to place.
Accelerated curing is any method by which high early age strength is achieved in concrete.These techniques are especially useful in the prefabrication industry, wherein high early age strength enables the removal of the formwork within 24 hours, thereby reducing the cycle time, resulting in cost-saving benefits. [1]
Portland cement clinker was first made (in 1825) in a modified form of the traditional static lime kiln. [2] [3] [4] The basic, egg-cup shaped lime kiln was provided with a conical or beehive shaped extension to increase draught and thus obtain the higher temperature needed to make cement clinker.