This limits the usefulness of austenitic stainless steel for containing water with higher than a few parts per million content of chlorides at temperatures above 50 °C (122 °F); mild steel cracks in the presence of alkali (e.g. boiler cracking and caustic stress corrosion cracking) and nitrates;
In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride. PREN is frequently specified when stainless steels will be exposed to seawater or other high chloride solutions. In some instances stainless steels with PREN-values > 32 may provide useful resistance to pitting corrosion in ...
Severe pitting corrosion problems caused by chloride ions on a truss beam of the Nandu River Iron Bridge (Hainan Province, China) leading to the complete rupture of a metallic element. Pitting corrosion , or pitting , is a form of extremely localized corrosion that leads to the random creation of small holes in metal.
AL-6XN (UNS designation N08367) is a type of weldable stainless steel that consist of an alloy of nickel (24%), chromium (22%) and molybdenum (6.3%) with other trace elements such as nitrogen. The high nickel and molybdenum contents of the AL-6XN alloy give it good resistance to chloride stress-corrosion cracking.
They provide better corrosion resistance, particularly chloride stress corrosion and chloride pitting corrosion, and higher strength than standard austenitic stainless steels such as A2/304 or A4/316. The main differences in composition, when compared with austenitic stainless steel is that duplex steels have a higher chromium content, 20–28% ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.