ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.
ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3). ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M.
High-strength low-alloy Structural steel A242 46 67 1.46 21 Low and intermediate tensile strength carbon steel plates A283 A 24 45-60 1.88 30 B 27 50-65 1.85 28 C 30 55-75 1.83 25 D 33 60-80 1.82 23 Cold-formed welded and seamless carbon steel structural tubing in rounds and shapes A500 Round Tubing A 33 45 1.36 25 B 42 58 1.38 23 C 46 62 1.35 21
The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
304 stainless steel cannot be heat treated—instead it can be strengthened by cold working. It is weakest in the annealed condition, and is strongest in the full-hard condition. The tensile yield strength ranges from 210 to 1,050 MPa (30,000 to 153,000 psi).
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).