Cutting speed may be defined as the rate at the workpiece surface, irrespective of the machining operation used. A cutting speed for mild steel of 100 ft/min is the same whether it is the speed of the cutter passing over the workpiece, such as in a turning operation, or the speed of the cutter moving past a workpiece, such as in a milling operation.
SFM is a combination of diameter and the velocity of the material measured in feet-per-minute as the spindle of a milling machine or lathe. 1 SFM equals 0.00508 surface meter per second (meter per second, or m/s, is the SI unit of speed). The faster the spindle turns, and/or the larger the diameter, the higher the SFM.
Material removal rate (MRR) is the amount of material removed per time unit (usually per minute) when performing machining operations such as using a lathe or milling machine. The more material removed per minute, the higher the material removal rate. [1] [2] The MRR is a single number that enables you to do this. It is a direct indicator of ...
Machinability is the ease with which a metal can be cut permitting the removal of the material with a satisfactory finish at low cost. [1] Materials with good machinability (free machining materials) require little power to cut, can be cut quickly, easily obtain a good finish, and do not cause significant wear on the tooling.
Superfinishing, also known as microfinishing [1] and short-stroke honing, is a metalworking process that improves surface finish and workpiece geometry. This is achieved by removing just the thin amorphous surface layer of fragmented or smeared metal left by the last process with an abrasive stone or tape; this layer is usually about 1 μm in magnitude.
Chemical milling or industrial etching is the subtractive manufacturing process of using baths of temperature-regulated etching chemicals to remove material to create an object with the desired shape. [1] [2] Other names for chemical etching include photo etching, chemical etching, photo chemical etching and photochemical machining. It is ...
Mill scale is a complex oxide that contains around 70% iron with traces of nonferrous metals and alkaline compounds. Reduced iron powder may be obtained by conversion of mill scale into a single highest oxide i.e. hematite (Fe 2 O 3) followed by reduction with hydrogen.
3D printing [3] Direct metal laser sintering [4] Filament winding, produces composite pipes, tanks, etc. [3] Fused deposition modeling [3] Inkjet Printing [5] Laminated object manufacturing [3] Laser engineered net shaping [3] Layered manufacturing [3] Rapid Induction Printing; Selective laser sintering [3] Spark plasma sintering ...