Shrinkage then introduces residual stresses and distortion. Distortion can pose a major problem since the final product is not the desired shape. To alleviate certain types of distortion, the workpieces can be offset so that after welding, the product is the correct shape. [19] The following pictures describe various types of welding distortion ...
The AWS defines welding PQR as a record of welding variables used to produce an acceptable test weldment and the results of tests conducted on the weldment to qualify a Welding Procedure Specification. For steel construction (civil engineering structures) AWS D1.1 is a widely used standard.
Many metals and thermoplastics can be welded, but some are easier to weld than others (see Rheological weldability). A material's weldability is used to determine the welding process and to compare the final weld quality to other materials. Weldability is often hard to define quantitatively, so most standards define it qualitatively.
Examples of submerged arc weld slag. Welding slag is a form of slag, or vitreous material produced as a byproduct of some arc welding processes, most specifically shielded metal arc welding (also known as stick welding), submerged arc welding, and flux-cored arc welding.
Dye penetrant inspection (DP), also called liquid penetrate inspection (LPI) or penetrant testing (PT), is a widely applied and low-cost inspection method used to check surface-breaking defects in all non-porous materials (metals, plastics, or ceramics).
Depending on the type of material, size and geometry of the object, and the forces applied, various types of deformation may result. The image to the right shows the engineering stress vs. strain diagram for a typical ductile material such as steel.
The weld structure can be examined by optical microscopy [3] [4] [5] and scanning electron microscopy. [ 6 ] [ 4 ] [ 5 ] [ 3 ] The computer finite element method (FEM) is used to predict the shape of the flash and interface and others, not only for rotary friction welding (RFW), [ 7 ] but also for friction stir welding (FSW), [ 8 ] [ 9 ] linear ...
The heat from the welding process and subsequent re-cooling causes this change from the weld interface to the termination of the sensitizing temperature in the base metal. The extent and magnitude of property change depends primarily on the base material, the weld filler metal, and the amount and concentration of heat input by the welding process.