Isothermal transformation diagrams (also known as time-temperature-transformation (TTT) diagrams) are plots of temperature versus time (usually on a logarithmic scale). They are generated from percentage transformation-vs time measurements, and are useful for understanding the transformations of an alloy steel at elevated temperatures.
Time-temperature transformation (TTT) diagram. The red line shows the cooling curve for austempering. Austempering is heat treatment that is applied to ferrous metals, most notably steel and ductile iron.
English: TTT diagram of the isothermal transformations of a hypoeutectoid carbon steel, together with its relationship with the Fe-C phase diagram of carbon steels. Without exact values, only for educational purposes.
Time-temperature transformation (TTT) diagram for steel. The red curves represent different cooling rates (velocity) when cooled from the upper critical (A3) temperature. V1 (quenching) produces martensite. V2 (normalizing) produces both pearlite and martensite, V3 (annealing) produces bainite mixed with pearlite.
Steel with a high carbon content will reach a much harder state than steel with a low carbon content. Likewise, tempering high-carbon steel to a certain temperature will produce steel that is considerably harder than low-carbon steel that is tempered at the same temperature. The amount of time held at the tempering temperature also has an effect.
Bainite is a plate-like microstructure that forms in steels at temperatures of 125–550 °C (depending on alloy content). [1] First described by E. S. Davenport and Edgar Bain, [2] [3] it is one of the products that may form when austenite (the face-centered cubic crystal structure of iron) is cooled past a temperature where it is no longer thermodynamically stable with respect to ferrite ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Type 2: This is the plot beginning with the transformation start point, cooling with specific transformation fraction and ending with a transformation finish temperature for all products against cooling rate or bar diameter of the specimen for each type of cooling medium.. TTT diagram for constant cooling rate transformations of steel.