Degraded concrete and rusted, exposed reinforcement bar (rebar) on Welland River bridge of the Queen Elizabeth Way in Niagara Falls, Ontario. Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or
Sulfur has long been known to contribute to damage. This is true for many materials such as metal corrosion, or concrete degradation. In King Lear, Shakespeare says: [5] There’s hell, there’s darkness, there is the sulphurous pit, Burning, scalding, stench, consumption; fie, fie, fie!
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
In sewerage areas where biogenic sulfide corrosion is expected, acid-resistant materials like calcium aluminate cements, PVC or vitrified clay pipe may be substituted to ordinary concrete or steel sewers. Existing structures that have extensive exposure to biogenic corrosion such as sewer manholes and pump station wet wells can be rehabilitated.
The initiation time is related to the rate at which carbonation propagates in the concrete cover thickness.Once that carbonation reaches the steel surface, altering the local pH value of the environment, the protective thin film of oxides on the steel surface becomes instable, and corrosion initiates involving an extended portion of the steel surface.
ASTM C1293: "Test Method for Concrete Aggregates by Determination of Length Change of Concrete Due to Alkali-Silica Reaction". It is a long-term confirmation test (1 or 2 years) at 38 °C in a water-saturated moist atmosphere (inside a thermostated oven) with concrete prisms containing the aggregates to be characterised mixed with a high-alkali ...