Nickel electroplating is a process of depositing nickel onto a metal part. Parts to be plated must be clean and free of dirt, corrosion, and defects before plating can begin. [3] To clean and protect the part during the plating process, a combination of heat treating, cleaning, masking, pickling, and etching may be used. [1]
Electroplating, also known as electrochemical deposition or electrodeposition, is a process for producing a metal coating on a solid substrate through the reduction of cations of that metal by means of a direct electric current.
The processed surface is then coated with electroless copper or nickel before further plating. This process gives useful (about 1 to 6 kgf /cm or 10 to 60 N /cm or 5 to 35 lbf /in) adhesion force, but is much weaker than actual metal-to-metal adhesion strength.
Electroless nickel-boron plating developed as a variant of the similar nickel-phosphorus process, discovered accidentally by Charles Adolphe Wurtz in 1844. [2]In 1969, Harold Edward Bellis from DuPont filed a patent for a general class of electroless plating processes using sodium borohydride, dimethylamine borane, or sodium hypophosphite, in the presence of thallium salts, thus producing a ...
Electroless nickel-phosphorus plating, also referred to as E-nickel, is a chemical process that deposits an even layer of nickel-phosphorus alloy on the surface of a solid substrate, like metal or plastic. The process involves dipping the substrate in a water solution containing nickel salt and a phosphorus-containing reducing agent, usually a ...
Electroless deposition is advantageous in comparison to PVD, CVD, and electroplating deposition methods because it can be performed at ambient conditions. [2] [6] The plating method for Ni-P, Ni-Au, Ni-B, and Cu baths are distinct; however, the processes involve the same approach. The electroless deposition process is defined by four steps: [2 ...
Chemical coloring of metals is the process of changing the color of metal surfaces with different chemical solutions. The chemical coloring of metals can be split into three types: electroplating – coating the metal surface with another metal using electrolysis. patination – chemically reacting the metal surface to form a colored oxide or ...
Electroless nickel immersion gold (ENIG or ENi/IAu), also known as immersion gold (Au), chemical Ni/Au or soft gold, is a metal plating process used in the manufacture of printed circuit boards (PCBs), to avoid oxidation and improve the solderability of copper contacts and plated through-holes.