4301-304-00-I and X5CrNi18-9, the ISO 15510 name and designation. UNS S30400 in the unified numbering system. A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent ...
Jindal Stainless Limited is an Indian stainless steel maker headquartered in New Delhi. It is a part of OP Jindal group. The firm has a melt capacity of 2.9 million tonnes per annum which makes it the largest stainless steel producer of India. Incorporated in 1970, it ranks among the top 5 stainless steel makers of the world. [6] [4] [5] [7]
Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel). [6] The Japanese equivalent grade of this material is SUS304.
In addition to the descriptive steel grade naming system indicated above, within EN 10027-2 is defined a system for creating unique steel grade numbers. While less descriptive and intuitive than the grand names they are easier to tabulate and use in data processing applications. The number is in the following format: x.yyzz(zz)
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Razor blade steel is a martensitic stainless steel with a composition of chromium between 12 and 14.5%, a carbon content of approximately 0.6%, and the remainder iron and trace elements. [ 1 ] [ 2 ] Shape