SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
A continuous cooling transformation (CCT) phase diagram is often used when heat treating steel. [1] These diagrams are used to represent which types of phase changes will occur in a material as it is cooled at different rates.
The phase diagram shows, in pressure–temperature space, the lines of equilibrium or phase boundaries between the three phases of solid, liquid, and gas. The curves on the phase diagram show the points where the free energy (and other derived properties) becomes non-analytic: their derivatives with respect to the coordinates (temperature and ...
Martensitic stainless alloys are hardenable by heat treatment, specifically by quenching and stress relieving, or by quenching and tempering (referred to as QT). [9] [10] The alloy composition, and the high cooling rate of quenching enable the formation of martensite. Untempered martensite is low in toughness and therefore brittle.Tempered ...
Flow Curve Analysis of 17–4 PH Stainless Steel under Hot Compression Test, comprehensive study of DRX; Constitutive relations to model the hot flow of commercial purity copper, chapter 6, doctoral thesis by V.G. García, UPC (2004) A review of dynamic recrystallization phenomena in metallic materials, Latest review paper on DRX
Type 630 is most common PH stainless, better known as 17-4; 17% chromium, 4% nickel. 650 through 653: Austenitic steels strengthened by hot/cold work. 660 through 665: Austenitic superalloys; all grades except alloy 661 are strengthened by second-phase precipitation.
Time-Temperature-Transformation diagram for two steels: one with 0.4% wt. C (red line) and one with 0.4% wt. C and 2% weight Mn (green line). P = pearlite, B = bainite and M = martensite. Isothermal transformation diagrams (also known as time-temperature-transformation ( TTT ) diagrams ) are plots of temperature versus time (usually on a ...