A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
The Rockwell hardness test is a hardness test based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1] There are different scales, denoted by a single letter, that use different loads or indenters.
Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ... Toggle the table of contents.
The Mohs scale of mineral hardness; The Vickers hardness test; The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale; The Rosiwal scale; The Meyer hardness test; The Knoop hardness test
Two scales that measures rebound hardness are the Leeb rebound hardness test and Bennett hardness scale. Ultrasonic Contact Impedance (UCI) method determines hardness by measuring the frequency of an oscillating rod. The rod consists of a metal shaft with vibrating element and a pyramid-shaped diamond mounted on one end. [4]
Conversion to SI units [ edit ] To convert the Vickers hardness number to SI units the hardness number in kilograms-force per square millimeter (kgf/mm 2 ) has to be multiplied with the standard gravity , g 0 {\displaystyle g_{0}} , to get the hardness in MPa (N/mm 2 ) and furthermore divided by 1000 to get the hardness in GPa.
Barcol hardness is measured on a scale from 0 to 100 with the typical range being between 50B and 90B. A measurement of 60B is roughly equivalent to a Shore hardness of 80D or a Rockwell hardness M100. [4] [6] As defined in ASTM D 2583 the scale divisions from 0-100 should each indicate a depth of 0.0076 mm or the equivalent 0.0003 inches. [7]
It determines hardness through the scale of penetration of an indenter, loaded on a material test-piece. It is one of several definitions of hardness in materials science. The hardness scale is expressed as the Brinell Hardness Number (BHN or BH) and was named for Johan August Brinell, who developed the method in the early 20th century.