AFm form inter alia when tricalcium aluminate 3CaO·Al 2 O 3, or C 3 A in CCN, reacts with dissolved calcium sulfate (CaSO 4), or calcium carbonate (CaCO 3). As the sulfate form is the dominant one in AFm phases in the hardened cement paste (HCP) in concrete, AFm is often simply referred to as Aluminate Ferrite monosulfate or calcium aluminate ...
Calcium aluminates phase diagram Crystal structure of dodecacalcium hepta-aluminate, 12CaO·7Al 2 O 3 (C 12 A 7). [1] Calcium aluminates are a range of materials [2] obtained by heating calcium oxide and aluminium oxide together at high temperatures. They are encountered in the manufacture of refractories and cements.
Monocalcium aluminate is formed when the appropriate proportions of calcium carbonate and aluminium oxide are heated together until the mixture melts. It melts incongruently at 1390 °C. The crystal is monoclinic and pseudohexagonal , and has density 2945 kg·m −3 .
Calcium aluminates can form complex salts in combination with different types of anions.Two series of calcium aluminates are known in cement chemistry: AFm and AFt phases, being respectively mono- or tri-substituted with a given divalent anion X (e.g. SO 2− 4, CO 2− 3, or hosting a divalent impurity such as SeO 2− 4 [3]...), or with two units of a monovalent anion, e.g. OH −, Cl − ...
Tricalcium aluminate Ca 3 Al 2 O 6, often formulated as 3CaO·Al 2 O 3 to highlight the proportions of the oxides from which it is made, is the most basic of the calcium aluminates. It does not occur in nature, but is an important mineral phase in Portland cement .
It represents a group of calcium aluminate hydrates. AFt has the general formula [Ca 3 (Al,Fe)(OH) 6 •12H 2 O] 2 •X 3 •nH 2 O where X represents a doubly charged anion or, sometimes, two singly charged anions. Ettringite is the most common and prominent member of the AFt group (X in this case denoting sulfate), and often simply called ...
So, CAC cement must not be confused with calcium sulfo-aluminate (CSA) cement containing calcium sulfate and invented later in 1936. [6] The main constituent, and also the most reactive phase, of calcium aluminate cements is the monocalcium aluminate (CaAl 2 O 4 = CaO · Al 2 O 3, also written as CA in the cement chemist notation).
Ye'elimite is the naturally occurring form of anhydrous calcium sulfoaluminate, Ca 4 (Al O 2) 6 SO 4.It gets its name from Har Ye'elim in Israel in the Hatrurim Basin west of the Dead Sea where it was first found in nature by Shulamit Gross, an Israeli mineralogist and geologist who studied the Hatrurim Formation.