The test is carried out using a metal mould in the shape of a conical frustum known as a slump cone or Abrams cone, that is open at both ends and has attached handles.The tool typically has an internal diameter of 100 millimetres (3.9 in) at the top and of 200 millimetres (7.9 in) at the bottom with a height of 305 millimetres (12.0 in).The cone is placed on a hard non-absorbent surface.
The flow table test or slump-flow test is a method to determine consistency of fresh concrete. Flow table test is also used to identify transportable moisture limit of solid bulk cargoes. [1] It is used primarily for assessing concrete that is too fluid (workable) to be measured using the slump test, because the concrete will not retain its ...
Abrams investigated the influence of the composition of concrete mixes on the strength of the end product. Some of the results of his research were: the definition of the concept of fineness modulus; the definition of the water–cement ratio; a concrete slump test for the
Concrete slump test; F. Flow table test This page was last edited on 2 December 2023, at 09:33 (UTC). Text is available under the Creative Commons Attribution ...
Workability can be measured by the concrete slump test, a simple measure of the plasticity of a fresh batch of concrete following the ASTM C 143 or EN 12350-2 test standards. Slump is normally measured by filling an "Abrams cone" with a sample from a fresh batch of concrete. The cone is placed with the wide end down onto a level, non-absorptive ...
Concrete has a limited lifespan between batching / mixing and curing. This means that ready-mixed concrete should be placed within 30 to 45 minutes of the batching process to hold slump and mix design specifications in the US, [15] though in the UK, environmental and material factors, plus in-transit mixing, allow for up two hours to elapse. [16]
The test hammer hits the concrete at a defined energy. Its rebound is dependent on the hardness of the concrete and is measured by the test equipment. By reference to a conversion chart, the rebound value can be used to determine the concrete's compressive strength. When conducting the test, the hammer should be held at right angles to the ...
The effect of the water-to-cement (w/c) ratio onto the mechanical strength of concrete was first studied by René Féret (1892) in France, and then by Duff A. Abrams (1918) (inventor of the concrete slump test) in the USA, and by Jean Bolomey (1929) in Switzerland.