6063 is the most common alloy used for aluminium extrusion. It allows complex shapes to be formed with very smooth surfaces fit for anodizing and is popular for visible architectural applications such as window frames, door frames, roofs, and sign frames. [ 3 ]
T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061 . The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.
It is produced in many tempers, some of which are 7075-0, 7075-T6, 7075-T651. The first 7075 was developed in secret by a Japanese company, Sumitomo Metal , in 1935, [ 3 ] but reverse engineered by Alcoa in 1943, after examining a captured Japanese aircraft.
Aluminium–copper alloys (AlCu) are aluminium alloys that consist largely of aluminium (Al) and traces of copper (Cu) as the main alloying elements. Important grades also contain additives of magnesium , iron , nickel and silicon ( AlCu(Mg, Fe, Ni, Si) ), often manganese is also included to increase strength (see aluminium-manganese alloys ).
The AlMgSi alloys are therefore understood in the standards as a separate group (6000 series) and not as a subgroup of aluminum-magnesium alloys that cannot be hardenable. AlMgSi is one of the aluminum alloys with medium to high strength, high fracture resistance, good welding suitability, corrosion resistance and formability. They can be ...