6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
English: The temperatures in this 6061 aluminum heat treat diagram are based off ASTM standard B918M−17a. The times for steps in the process depend on the size of the part. The times for steps in the process depend on the size of the part.
Heat treatment provides an efficient way to manipulate the properties of the metal by controlling the rate of diffusion and the rate of cooling within the microstructure. Heat treating is often used to alter the mechanical properties of a metallic alloy, manipulating properties such as the hardness, strength, toughness, ductility, and ...
In the aluminum industry, the process is also called chemical film [13] or yellow iridite, [13] Commercial trademarked names include Iridite [13] and Bonderite [14] (formerly known as Alodine, or Alocrom in the UK). [15] The main standards for chromate conversion coating of aluminium are MIL-DTL-5541 in the US, and Def Stan 03/18 in the UK.
Forming operations where a blow torch is used can reverse or remove the effects of heat treatment. No visual signs reveal how the material is internally damaged. Much like welding heat treated, high strength link chain, all strength is now lost by heat of the torch. The chain is dangerous and must be discarded. [citation needed]
AlMgSi is one of the hardenable aluminum alloys, i.e. those that can become firmer and harder through heat treatment. This curing is largely based on the excretion of magnesium silicide (Mg 2 Si). The AlMgSi alloys are therefore understood in the standards as a separate group (6000 series) and not as a subgroup of aluminum-magnesium alloys that ...
Operating a vacuum heat treating furnace, c. 1959–1962. A vacuum furnace is a type of furnace in which the product in the furnace is surrounded by a vacuum during processing. The absence of air or other gases prevents oxidation, heat loss from the product through convection, and removes a source of contamination